SLPF06 High Performance Shrink Film

SLPF06 High-Performance Shrink Film is an exceptional thermal shrink film designed to address virtually all challenges encountered during the shrink-wrapping process. It excels in low-temperature environments, offering a low shrink initiation temperature and rapid shrinkage, with shrink ratios exceeding 70%. This ensures SLPF06 delivers outstanding packaging results even under the most demanding conditions.

The film’s excellent slip properties make it ideal for rapid box packing of shrink-wrapped flat or boxed items, preventing adhesion or abrasion. Additionally, SLPF06 features a wide range of shrink temperatures, superior heat-sealing capabilities, and low shrink force. Among non-cross-linked polyolefin shrink films, SLPF06 stands out for its superior packaging performance and is suitable for use on any packaging machine.

• Available Thicknesses: 9 microns, 11 microns, 14 microns, and 19 microns.

Features of SLPF06 High Performance Shrink Film

Achieves perfect shrinkage at 120°C.
Operates effectively within a wide temperature range of 110°C to 180°C.
Delivers rapid shrinkage in just 1.5 seconds.
Offers an excellent shrink ratio.
Features a low temperature for seal initiation.
Provides high-strength seals.
Boasts high tear resistance.
Maintains strong performance in low-temperature shrink force.
Ensures good hot slip properties post-shrinkage.
Compatible with electrostatic sealing.

Performance Chart of SLPF06 High Performance Shrink Film

TEST ITEM		UNIT	ASTM TEST	TYPICAL VALUES
THICKNESS				10μm	12μm	15μm	19μm
TENSILE
Tensile Strength(MD)		N/mm²	D882	80	75	75	68
Tensile Strength(TD)				80	65	65	63
Elongation(MD)		%		95	95	100	93
Elongation(TD)				80	85	93	85
TEAR
MD		g	D1922	12.5	14.5	16.5	24.0
TD				11.5	15.0	16.0	23.0
SEAL STRENGTH
MDHot Wire Seal		N/mm	F88	0.72	0.68	0.75	0.95
TDHot Wire Seal				0.65	0.65	0.72	0.91
COF(Film to Film)
Dynamic			D1894	0.18	0.21	0.17	0.16
Static				0.2	0.22	0.19	0.18
Static(Hot Slip)@60℃				0.28	0.31	0.28	0.26
OPTICS
Haze			D1003	3.2	3.5	3.9	4.3
Clarity			D1746	97.5	97.5	98.0	97.0
Gloss @45Deg			D2457	80.5	82.0	84	84.0
BARRIER
Oxygen Transmission Rate		cc/m²/day	D3985	13500	12900	11700	9600
Water Vapor Transmission Rate		gm/m²/day	F1249	58	52	45	38
SHRINKAGE PROPERTIES				MD	TD	MD	TD	MD
Free Shrinkage	80℃	%	D2732	20	23	20	15	17
	90℃			28	35	32	22	28
	100℃			44	48	47	42	47
	110℃			57	57	56	54	55
	120℃			65	64	64	62	62
	130℃			70	69	67	67	65
–
Shrink Tension	90℃	MPa	D2838	1.80	2.10	2.2	1.95	2.1
	100℃			2.15	2.25	2.4	2.4	2.5
	110℃			2.50	2.70	2.65	2.75	2.85
	120℃			2.40	2.40	2.50	2.60	2.6
Note: The information above is based on internal evaluations of our company and is for reference only.