SLP101 Low Temperature Cross-Linked Shrink

SLP101 Low Temperature Cross-Linked Shrink

SLP101 is a superior soft cross-linked heat shrink film distinguished by its outstanding low-temperature shrink capabilities. This high-performance polyolefin shrink film boasts an impressive set of features including a high shrink ratio, exceptional clarity, robust seal strength, excellent toughness, and superior resistance to sagging, making it a standout choice for shrink packaging in our product line.

Ideal for wrapping a diverse array of products, SLP101excels in packaging soft items such as books, as well as irregularly shaped goods. Its capability to perform under low temperatures ensures delicate, heat-sensitive products are protected efficiently, and also helps to prevent the “ribbing” effect at the edges of boxed items.
SLP101 is compatible with all types of shrink packaging machinery.

Available Thicknesses: 11 microns, 15 microns, and 19 microns.

Performance Chart of SLP101 Low Temperature Cross-Linked Shrink

TEST ITEM		UNIT	ASTM TEST	TYPICAL VALUES
THICKNESS				11μm	15μm	19μm
TENSILE
Tensile Strength(MD)		N/mm²	D882	95	90	90
Tensile Strength(TD)				85	85	85
Elongation(MD)		%		120	115	120
Elongation(TD)				115	110	115
TEAR
MD		g	D1922	13.0	17.5	21.0
TD				14.0	18.0	23.0
SEAL STRENGTH
MDHot Wire Seal		N/mm	F88	1.3	1.55	1.75
TDHot Wire Seal				1.35	1.65	1.75
COF(Film to Film)
Dynamic			D1894	0.23	0.20	0.24
Static				0.25	0.21	0.23
OPTICS
Haze			D1003	2.40	2.50	2.80
Clarity			D1746	99.0	98.8	98.0
Gloss @45Deg			D2457	88.0	88.0	87.5
BARRIER
Oxygen Transmission Rate		cc/m²/day	D3985	9600	8700	5900
Water Vapor Transmission Rate		gm/m²/day	F1249	32.1	27.8	19.5
SHRINKAGE PROPERTIES				MD	TD
Free Shrinkage	100℃	%	D2732	17	23
	110℃			34	39
	120℃			59	66
	130℃			79	77
				MD	TD
Shrink Tension	100℃	MPa	D2838	1.70	1.85
	110℃			1.90	2.55
	120℃			2.50	3.20
	130℃			2.70	3.5
Note: The information above is based on internal evaluations of our company and is for reference only.