SLPF01 Polyolefin Shrink Film

SLPF01Polyolefin Shrink Film is a high-performance, versatile packaging solution that offers exceptional clarity and strength. This bi-directional shrink film ensures even and reliable shrinkage, enhancing the appearance and security of packaged items. It retains flexibility and softness at the edges even in low temperatures, preventing brittleness. The film is environmentally friendly, producing no harmful emissions during use.

Perfect for a variety of packaging applications, SLPF01 is especially effective as both a folded and a single sheet film. It is compatible with most automatic and semi-automatic packaging machines, making it an economical and widely adaptable option for your packaging needs.

Available Thicknesses: 12 microns, 15 microns, 19 microns, 25 microns, 30 microns.

Performance Chart of SLPF01 Polyolefin Shrink Film

TEST ITEM		UNIT	ASTM TEST	TYPICAL VALUES
THICKNESS				12um	15um	19um	25um	30um
TENSILE
Tensile Strength(MD)		N/mm²	D882	115	110	110	95	85
Tensile Strength(TD)		N/mm²		110	105	105	90	80
Elongation(MD)		%		115	120	125	130	130
Elongation(TD)				110	115	115	125	125
TEAR
MD		g	D1922	10.5	14.5	17.5	23.5	28.5
TD		g	D1922	10	13.5	16.0	23	27
SEAL STRENGTH
MDHot Wire Seal		N/mm	F88	0.65	0.81	1.03	1.25	1.55
TDHot Wire Seal		N/mm	F88	0.68	0.86	1.06	1.30	1.65
COF(Film to Film)
Dynamic			D1894	0.23	0.22	0.22	0.25	0.25
Static			D1894	0.24	0.23	0.24	0.26	0.25
OPTICS
Haze			D1003	2.2	2.6	3.2	3.9	4.5
Clarity			D1746	98.5	98.0	97.0	95.0	92.0
Gloss @45Deg			D2457	85.5	87.0	83.5	81.5	80.0
BARRIER
Oxygen Transmission Rate		cc/m²/day	D3985	11300	10800	7200	5400	4500
Water Vapor Transmission Rate		gm/m²/day	F1249	45.5	38.5	26.5	22.5	20.5
SHRINKAGE PROPERTIES				MD	TD	MD	TD
Free Shrinkage	100℃	%	D2732	22	31	20	28
	110℃			38	45	34	45
	120℃			58	63	57	60
	130℃			65	67	64	65

Shrink Tension	100℃	Mpa	D2838	1.80	2.65	1.85	2.55
	110℃			2.70	3.50	2.85	3.65
	120℃			2.80	3.65	2.90	3.60
	130℃			2.60	3.15	2.70	3.05

Note: The information above is based on internal evaluations of our company and is for reference only.